Good Form-ability 3003 H22 H14 aluminum sheet 5083 aluminium metal
plates 5052 flat aluminum sheet plate
3003 aluminum sheet Designed for sheet metal work, fuel tanks, and other applications
that require a slightly higher strength than 1100 series aluminum.
The 3003 aluminum sheet is a pure aluminum that is used
commercially. It’s moderately strong and can resist corrosion.
Although it’s not heat treatable, it can be easily welded. It can
also be formed using hot working and cold working methods. It is
one of the alloys that have great machinability. When being forged
with heat, it’s best for the temperature to range between 950
degrees and 500 degrees Fahrenheit. It’s best to use a filler rod
like the AL 4043 when welding together 3003 aluminum with alloys
like 5052, 6062 and 6061.
This aluminum grade can also be easily cold worked and has
annealing capabilities, which should be done at 775 degrees
Fahrenheit either during or after cold working. Afterward, air
cooling should be allowed. The conductivity of 3003 alloys is 40
percent of copper.
The reason this metal is widely used is because it is affordable
and strong. Compared to the 1100 series of alloys, 3003 aluminum is
20 percent stronger. This is due to it being integrated with 1.20
percent manganese. It is considered a pure aluminum and is
frequently used in various applications, such as for storage tanks,
tool boxes, walkways, truck beds, decorative trim and chemical
equipment. It can also be used to create fan blades, siding,
trailer components, kitchen equipment, cooking utensils and for
signage applications.
3003 aluminum has a lot of great characteristics that make it a
popular choice. Other than being weldable and corrosion-resistant,
it also has a surface that has a highly polished finish, making it
an attractive choice. Although thin, it cannot be bent easily,
instead requiring special tools to do so
Aluminum alloy plate Sheet 3003 H14 Bare is an excellent choice for chemical equipment and general sheet
metal projects due to its superior corrosion resistance and good
workability. Aluminum 3003 H14 bare sheet works well in fabrication and decorative architectural uses
because it is highly workable, formable, and weldable, while being
capable of withstanding outdoor weather
Alloy 3003 is fairly low strength but it can be hardened to a
significant degree by cold working, enabling a series of “H”
tempers. Alloy 3003 is also produced as a bright finish treadplate
(also known as chequer plate) with industrial and decorative
applications.
3003-H14 Aluminum alloy plate is alloyed with 1.20% manganese, which increases the strength of
3003 over commercially pure aluminum (1100 series).3003 has
excellent workability, weldability, and good corrosion resistance
3003 Aluminum is one of the most widely used of all aluminum
alloys. It is a general purpose aluminum, with moderate strength,
good workability and weldability, and excellent corrosion
resistance. 3003 is a non heat treatable grade, and it may be deep
drawn, or spun, welded, or brazed.
Alloy Available: 1050 1060 1100 3003, 3105, 5052, 5005, 5754 5083
5182, 6061 6063 6082, 7075, 8011…
Temper: HO, H111,H12, H14, H24,H 32, H112, T4, T6, T5,T651
Surface:Mill/Emboss/Diamond/2bar/3bars/Bright
Thickness: 0.2mm to 300mm
Width: 30mm to 2300mm
Length:1000mm to 10000mm.
Aluminum stair tread sheet, Aluminum tread Brite plate,Aluminum
checker plate manufacturers, Perforated aluminum sheet
china,Diamond sheet manufacturers, Aluminum tread plate
manufacturers
| Chemical Analysis of aluminum alloy Plate |
| Alloy | Si | Fe | Cu | Mn | Mg | Cr | Ni | Zn | Ti | Al |
| 1050 | 0.25 | 0.4 | 0.05 | 0.05 | 0.05 | - | - | 0.05 | 0.03 | Remains |
| 1060 | 0.25 | 0.35 | 0.05 | 0.03 | - | - | - | - | - | Remains |
| 1070 | 0.2 | 0.25 | 0.04 | 0.03 | 0.03 | - | - | - | - | Remains |
| 1100 | 0.95 | 0.95 | 0.05-0.2 | 0.05 | - | - | 0.1 | - | - | Remains |
| 1200 | 1 | 1 | 0.05 | 0.05 | - | - | - | 0.1 | 0.05 | Remains |
| 3003 | 0.6 | 0.7 | 0.05-0.2 | 1.0-1.5 | - | - | - | 0.1 | - | Remains |
| 5005 | 0.3 | 0.7 | 0.2 | 0.2 | 0.5-1.1 | 0.1 | - | 0.25 | - | Remains |
| 5042 | 0.2 | 0.35 | 0.15 | 0.2--.5 | 3.0-4.0 | 0.1 | - | 0.25 | 0.1 | Remains |
| 5052 | 0.25 | 0.4 | 0.1 | 0.1 | 2.2-2.8 | 0.15-0.35 | - | 0.1 | - | Remains |
| 5083 | 0.4 | 0.4 | 0.1 | 0.4-1.0 | 4.0-4.9 | 0.05-0.25 | - | 0.25 | - | Remains |
| 5754 | 0.4 | 0.4 | 0.1 | 0.5 | 2.6-3.6 | 0.3 | - | 0.2 | - | Remains |
| 6061 | 0.4-0.8 | 0.7 | 0.15-0.4 | 0.15 | 0.8-1.2 | 0.04-0.35 | - | 0.25 | - | Remains |
| 6063 | 0.2-0.6 | 0.35 | 0.1 | 0.1 | 0.45 | 0.1 | - | 0.1 | - | Remains |
| 6082 | 0.7-1.3 | 0.5 | 0.1 | 0.4-1.0 | 0.6-1.2 | 0.25 | - | 0.2 | - | Remains |
| 7050 | 0.12 | 0.15 | 2.0-2.6 | 0.1 | 1.9-2.6 | 0.04 | - | 5.7-6.7 | 0.06 | Remains |
| 7075 | 0.4 | 0.5 | 1.2-2.0 | 0.3 | 2.1-2.9 | 0.18-0.28 | - | 5.1-6.1 | 0.2 | Remains |